Ref: ISO-PFCC-203/ DIN-Hgw-2083/ JIS-PL-PLL/ NEMA-L
1. COMPOSITION AND PRESENTATION NEMA-L is a stratified insulator made from cotton cloth and phenolic resin. At delivery time the presentation of the sheets is as follows: - Maximum sizes: 1020 X 2040 mm. - Thickness: From 0.50 mm - Colour: Dark Brown - Surfaces: Shining - On demand we can deliver strips or finished components. 2. PROPERTIES AND APPLICATIONS - Excellent mechanical properties - High resistance to blows and vibrations. - High resistance to friction, for general industrial applications Mechanized pieces of big size for mechanical applications such as ball bearing, silent gearing for modulessuperior to 2.5, ball bearing caps, pulleys. It also can be used as insulating construction parts in electrical equipment.
3. SIZES (mm)
Width |
450 ¨C 1020 |
¡À 15 |
Length |
> 980 - 2040 |
¡À 25 |
4. NORMAL THICKNESS (mm)
Normal Thickness |
Tolerance |
Normal Thickness |
Tolerance |
0.8
1.0
1.2
1.6
2.0
2.5
3.0
4.0
5.0
6.0
8.0 |
¡À0.19
¡À0.20
¡À0.22
¡À0.24
¡À0.26
¡À0.29
¡À0.31
¡À0.36
¡À0.42
¡À0.46
¡À0.55 |
10
12
14
16
20
25
30
35
40
45
50 |
¡À0.63
¡À0.70
¡À0.78
¡À0.85
¡À0.95
¡À1.10
¡À1.22
¡À1.34
¡À1.45
¡À1.55
¡À1.65 |
If need un-normal thickness, the tolerance will be confirmed by the seller and the buyer each other before placing the order.
5. MAIN TECHNICAL CHARACTERISTICS / SHEETS NEMA-L
ITEMS |
CONDITIONS |
NORMS |
VALUES |
Resistance to traction( parallel ) |
20¡æ |
UNE53189-2 |
65 MPa min. |
Resistance to flexion( perpendicular ) |
20¡æ |
UNE53189-3 |
100 MPa min. |
Impact strength (¡Ý4mm/charpy¡Ý4mm in thickness ) |
20¡æ |
UNE53189-5 |
7.0 KJ/m2 min. |
Bonding strength |
20¡æ |
-- |
-- |
Dielectric strength 1'( perpendicular ) |
In transformer oil at 90 ¡À 2¡æ |
UNE53189-13 |
1.0 MV/m min. |
Dielectric strength 1'( parallel ) |
In transformer oil at 90 ¡À 2¡æ |
UNE53189-13 |
15 KV min. |
Insulating resistance after impregnated in water |
in water |
UNE53189-12/UNE21-306 |
1.0 X 106 ¦¸ min. |
Resistance to heat s/Martens |
-- |
DIN 53458 |
125¡æ |
Thermic Class |
-- |
CEI Pub.85 |
E ¨C 120¡æ |
Water absorption rate (D-24/23) |
24 h. |
ISO1642/UNE53189 |
2.50% |
Specific weight |
20¡æ |
DIN 53479 |
1.30-1.40 g/cm3 |
|